Secondary recrystallization textures and their origin in cold-rolled single crystals of silicon iron

Abstract

Single crystals in three different orientations were cold rolled 70 per cent and were annealed to produce both primary and secondary recrystallization structures. A detailed study of changes in grain size and in orientation was made using metallographic, X-ray, and magnetic torque methods. The orientations of a few early forming primaries were determined. It was concluded that relatively large primary grains in orientations deviating markedly from the primary recrystallization texture grow into secondary grains having specific preferred orientations and that the driving force for secondary recrystallization comes from grain boundary energy. Drei Einkristalle mit verschiedener kristallographischer Orientierung wurden 70 prozent kaltverformt und dann geglüht um primäre and sekondäre Rekristallisationstexturen zu erzeugen. Eine detaillierte Untersuchung der Korngrösse and der Orientierung der Kristallite wurde mit Hilfe von metallographischen, röntgenographischen and magnetischen Messungen durchgeführt. Es wurde aus diesen Untersuchungen geschlossen, class relativ grosse primäre Kristallite, die in ihrer kristallographischen Orientierung merkbar von der primären Rekristallisationstextur abweichen, als sekundäre Kristallite mit spezifischen, bevorzugten, Orientierungen weiterwachsen, and class der Ursprung der Kräfte, die zur sekundären Rekristallisation treiben, in der spezifischen Energie der Korngrenzen liegt.