Abstract
To prevent gas mixing and leakage during solid oxide fuel/electrolyzer cell operation, the interconnect/seal glass interface should bond well and remain stable. A SrO–La 2O 3–Al 2O 3–SiO 2 (SABS-0) seal glass has been bonded to bare Crofer 22 APU alloy and (Mn,Co) 3O 4 coated Crofer 22 APU alloy. The stability of the interconnect/SABS-0 interface has been studied in air and H 2/H 2O atmospheres at 800 °C for 1000 h. The interconnect/seal glass interaction involves the oxidation of the bare and (Mn,Co) 3O 4 coated Crofer 22 APU alloy surfaces, inter-diffusion of elements, chemical reaction, and the devitrification of the SABS-0 glass. The study shows that the thermal treatment atmosphere greatly affects the interfacial stability of both bare Crofer 22 APU/SABS-0 and (Mn,Co) 3O 4 coated Crofer 22 APU/SABS-0 samples. The interfacial stability is better in the H 2/H 2O atmosphere for both samples. The instability of the (Mn,Co) 3O 4 coating under the thermal treatment conditions degrades the interfacial compatibility of the (Mn,Co) 3O 4 coated Crofer 22 APU/SABS-0 sample.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.