Abstract
Silver metallization pastes for crystalline silicon PV cells containing nanosized metallic zinc were found to be superior to commercial pastes containing micrometer-sized metallic zinc and micrometer sized zinc oxide in terms of efficiency and firing window. Efficiency performance decreases as the size of the particles increases: nano-Zn > 3.6 μm Zn > 4.4 μm Zn. Advanced electron microscopy techniques were used to investigate the interfacial microstructure between the front-side contact and the Si emitter of nanosized zinc additive based cells fired at temperatures from below to above optimal. These microstructural observations confirmed the possibility of a tunneling mechanism of current flow (a "nano-Ag colloid assisted tunneling" model) in the absence of Ag crystallites. Contact resistance maps were used to guide sampling, leading to a better understanding of the relationship between microstructure and contact resistance. Low contact resistance and higher cell efficiency, especially at under- and overfiring temperature conditions, are due to more uniform silicon nitride etching obtained through the use of nanosized metallic zinc additives.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.