Abstract
Low-temperature plasma nitriding is a thermochemical surface treatment that promotes surface hardening and wear resistance enhancement without compromising the corrosion resistance of sintered austenitic stainless steels. Hollow cathode radiofrequency (RF) plasma nitriding was conducted to evaluate the influence of the working pressure and nitriding time on the microstructure and thickness of the nitrided layers. A group of samples of sintered 316L austenitic stainless steel were plasma-nitrided at 400 °C for 4 h, varying the working pressure from 160 to 25 Pa, and the other group was treated at the same temperature, varying the nitriding time (2 h and 4 h) while keeping the pressure at 25 Pa. A higher pressure resulted in a thinner, non-homogeneous nitrided layer with an edge effect. Regardless of the nitriding duration, the lowest pressure (25 Pa) promoted the formation of a homogenously nitrided layer composed of nitrogen-expanded austenite that was free of iron or chromium nitride and harder and more scratching-wear-resistant than the soft steel substrate.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.