Abstract Three kinds of carbon black, HAF (high abrasion furnace, N330), MT (medium thermal, N990), and graphitized MT were observed with the scanning tunneling microscope (STM), the transmission electron microscope (TEM), and the scanning electron microscope (SEM) All the STM images are formed from measurements of the x, t, and z position of points on the surface of the particle. The STM images of carbon blacks were compared to transmission electron microscope (TEM) photographs. Pitted and stepped bumps were observed on the surface of HAF carbon black. The surface of MT carbon black was more rough and disorganized At the atomic scale, ordered structure was found on the surface of HAF carbon-black particles Graphitized MT carbon-black particles were faceted polyhedra. Some facets were smooth while others had multiple terraces. The surface of graphitized MT carbon black was so well ordered that a lattice of carbon atoms similar to HOPG (highly ordered pyrolytic graphite) was observed on the smooth facets.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have