Abstract
Rechargeable aqueous zinc-metal batteries (ZMBs) are considered as potential energy storage devices for stationary applications. Despite the significant developments in recent years, the performance of ZMBs is still limited due to the lack of advanced cathode materials delivering high capacity and long cycle life. In this work, we report a low-temperature and scalable synthesis method following a surfactant-assisted route for preparing manganese-doped hydrated vanadium oxide (MnHVO-30) and its application as the cathode material for ZMB. The as-prepared material possesses a porous architecture and expanded interlayer spacing. Therefore, the MnHVO-30 cathode offers fast and reversible insertion of Zn2+ ions during the charge/discharge process and delivers 341 mAh g-1 capacity at 0.1 A g-1. Moreover, the MnHVO-30||Zn cell retains 82% of its initial capacity over 1200 stability cycles, which is higher compared to that of the undoped system. Besides, a quasi-solid-state home-made pouch cell with an area of 3.3 × 1.6 cm2 and 3.6 mg cm-2 loading is assembled, achieving 115 mAh g-1 capacity over 100 stability cycles. Therefore, this work provides an easy and attractive way for preparing efficient cathode materials for aqueous ZMBs.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.