Sandwich-structured nanocomposite constructed by fabrication of exfoliation α-ZrP nanosheets and cobalt porphyrin utilized for electrocatalytic oxygen reduction

Abstract

Exfoliation/restacking route was adopted to investigate layer-by-layer self-assembly of α-ZrP/CoTMPyP [5, 10, 15, 20-tetrakis (N-methylpyridinium-4-yl) porphyrinato cobalt (III)] sandwich-structured nanocomposite in our research. The well-dispersed α-ZrP colloidal suspension in tetra-n-butylammonium hydroxide (TBA+OH−) aqueous solution whose zeta potential value is −40.1 mV was obtained. Besides, supported by XRD, IR, UV–vis, SEM, TEM, and TG-DTA, the CoTMPyP molecules were successfully introduced into the lamellar spacing of α-ZrP host material. Cyclic voltammetry measurements of α-ZrP/CoTMPyP hybrid film suggested the self-assembled product showed excellent electrocatalytic activities toward oxygen reduction with the reduction peak potential shifting from −0.692 V (bare glass carbon electrode) to −0.203 V (modified electrode). Moreover, the curves of the reduction peak current and the square root of scan rate presented good linear relationship, implying a diffusion-controlled process.