Abstract
Ni-doped ZnO thin films (Ni concentration up to 10 mol%) were generated on Si (100) substrates by a sol-gel technique. The films showed wurtzite structure and no other phase was found. The chemical state of Ni was found to be bivalent by X-ray photoelectron spectroscopy. The results of magnetic measurements at room temperature indicated that the films were ferromagnetic, and magnetic moment decreased with rise of Ni concentration. The magnetization of Ni (10 mol%)-doped ZnO film annealed in nitrogen was lower than that annealed in argon, suggesting that the density of defects had an effect on ferromagnetism.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.