Abstract
The fatigue crack propagation (FCP) behavior of Inconel 718 alloy manufactured by laser powder bed fusion (L-PBF) was studied at 25 and 650 °C, and compared to those of conventionally processed counterpart. The FCP rates of L-PBF Inconel 718 alloy were found to be significantly higher than those of conventionally processed counterpart at 25 °C in low and intermediate ΔK regimes. The FCP rates decreased in near-threshold ΔK regime at 650 °C, while the reversal occurred above ΔK of 7 MPa√m, as compared to those at 25 °C. The FCP behavior of L-PBF Inconel 718 alloy was discussed based on micrographic and fractographic analyses.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.