Surfaces of mechanical components under combined rolling and sliding motions may be subjected to accelerated contact fatigue failure due to increased number of microscopic stress cycles and pressure peak heights caused by rough-surface asperity contacts. Available rolling contact fatigue (RCF) theories were developed mainly for rolling element bearings, for which the effect of sliding is usually insignificant. In various types of gears, however, considerable sliding exist in the critical tooth contact area below the pitch line, where excessive wear and severe pitting failures originate. Ignorance of sliding is most likely the reason why the conventional RCF models often overestimate gear fatigue life. This paper studies the effect of sliding motion on the contact fatigue life of surfaces with sinusoidal roughness that mimicks the topography from certain manufacturing processes. A set of simple equations for stress cycle counting is derived. Mixed elastohydrodynamic lubrication simulations are executed with the considerations of normal loading and frictional shear. Relative fatigue life evaluations based on a subsurface stress analysis is conducted, taking into account the two sliding-induced mechanisms, which are the greatly increased number of stress cycles and the pressure peak heights due to surface interactions. Obtained results indicate that sliding leads to a significant reduction of contact fatigue life, and rough surface asperity contacts result in accelerated pitting failure that needs to be considered in life predictions for various mechanical components.

Talk to us

Join us for a 30 min session where you can share your feedback and ask us any queries you have

Schedule a call

Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.