Abstract

IF steel was homogeneously cold rolled between 30-95% reduction in thickness. The global cold rolling textures showed a gradual strengthening of both stable α and γ components with increasing reduction until ~80% after which γ remained effectively unchanged but α components intensified until 95% reduction of thickness. Deformation Banded (DB) and also fragmented microstructures were found exclusively in γ grains up until about 85% reduction after which DB was unexpectedly detected in α grains, becoming significant after 95% reduction. This is in sharp contrast with the rather undifferentiated microstructures found in α grains at low to medium levels of deformation. At lower reductions the annealing texture was a weak α, but the γ component increased with rolling strain and became dominant at ~80% rolling deformation. A peak type γ recrystallisation texture with orientations ranging from {554}<225> to {111}<123> was found in the 95% rolled sample. In addition to this a {411}<148> component began to intensify, reading 5R at 95% reduction. Microstructural analysis showed that DB provided the lattice curvature for nucleation in the α fibre.

Full Text
Paper version not known

Talk to us

Join us for a 30 min session where you can share your feedback and ask us any queries you have

Schedule a call

Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.