Abstract
The effect of Cu-Sn coating on steel towards improving the adhesion between steel and typical styrene butadiene rubber (SBR) based tyre bead composition has been investigated in this work. Steel coupons were coated with varying compositions of Cu-Sn via immersion coating, where the electrolyte bath composition was varied. Chemical analysis of the coatings using ICP-OES confirmed increase in Sn content with increasing SnSO4 concentration in the coating baths, keeping other parameters constant. No change in the coating weight was observed with change in Sn concentration in the coatings. Bare spots on the coating surface was observed under SEM XPS analysis confirmed formation of Fe oxide at the bare locations. The coated steel plates were vulcanized with SBR based rubber and peel strength was measured. The results confirmed an optimum Sn concentration of 3 - 4 wt% in the coatings up to which an increase (~ 25%) in adhesion strength was exhibited compared to only Cu coatings. Stereo-microscopic analysis of the peel tested samples validated mixed mode i.e. both adhesive and cohesive modes of failure.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.