Abstract
The effect of shear history on structure development during post-processing annealing was studied using poly(lactic acid) PLA. Since PLA shows a low crystallization rate, quenched films had no crystallinity. Moreover, molecular orientation was not detected in the films. During the annealing procedure beyond its glass transition temperature, however, molecular orientation to the flow direction occurred with the crystallization growth in the films having an appropriate shear history. This peculiar crystal growth during the annealing was most probably attributed to the crystallization from extended chain crystals generated during the applied shear history, although the amount of extended chain crystals was low. The results obtained in this study should be noted because the molecular orientation proceeded due to the annealing history applied. Furthermore, this phenomenon will be used to suppress dimensional change and increase product rigidity.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.