Abstract
Isolation of microstructural and microchemical effects on irradiation assisted stress corrosion cracking (IASCC) was attempted by means of low-dose high-temperature neutron irradiation in a material test reactor to get better understanding on IASCC. Microstructure, grain boundary segregation, hardness and SCC susceptibility were examined on stainless steels irradiated to 0.8 dpa at around 673 K. The irradiation caused well-developed grain boundary segregation without notable hardening or microstructural changes. No IASCC was found in 593 K hydrogenated water whereas the steels were highly susceptible to IASCC in 561 K oxygenated water. The results suggest that grain boundary segregation, probably Cr depletion, is sufficient to cause IASCC in oxygenated water and that other radiation-induced changes such as microstructure and hardening are required for IASCC in hydrogenated water.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.