Abstract
Nanocrystalline silicon (nc-Si:H) thin-film n-i-p solar cells were constructed on flexible stainless steel substrates by plasma-enhanced chemical vapor deposition. Influence of the n-type seed-layer on the microstructural evolution of the subsequent intrinsic nc-Si:H absorbers and the resultant performance of nc-Si:H solar cells was investigated. The crystalline volume fraction of the seed-layer can be effectively controlled by varying the hydrogen (H2) to silane (SiH4) gas flow ratio. Defect-dense amorphous regions were observed at the initial growth stage of the i-layers deposited on low crystalline volume fraction (Xcn) n-type seed-layers. Increasing the Xcn reduced the amorphous region at the n/i interface of the i nc-Si:H layers, evidenced by Raman scattering and transmission electron microscopy (TEM) measurements.Elimination of the defect-rich amorphous region within the i-layer by depositing the nc-Si:H solar cells on highly crystalline seed-layer caused significant improvements in the short circuit current density (Jsc) and fill factor (FF). This is mainly due to the enhancement of long-wavelength light response and extraction efficiency of photo-carrier charges. The nc-Si:H solar cells prepared on a highly crystalline seed-layer (Xcn=73%) exhibited a 65.6% higher conversion efficiency than those on the n-type amorphous layers (Xcn=0%).
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.