Abstract
In this study, a surface hardening method for Cr–C deposits using flame heating for a short period is proposed. The hardness and wear resistance behavior of as-plated and flame-heated Cr–C deposits were investigated. The Cr–C deposits were electroplated on high carbon tool steel in a bath with trivalent chromium ions. Experimental results show that Cr–C deposits with an extremely high hardness of ca. 1700 Hv can be achieved after reduction-flame heating for 1 s. Meanwhile, the wear resistance of Cr–C deposited steel was improved after flame heating. To increase the wear resistance and bonding strength of the Cr–C deposited specimen, pre-electrodeposition of a thin Ni deposit between the Cr–C deposit and the steel substrate is recommended. A Ni undercoat with a thickness of few micrometers could reduce the crack density in the Cr–C deposit and increase the bonding strength between the Cr–C deposit and the steel substrate. As determined by a microstructure study, the as-plated Cr–C deposit has an amorphous structure, but transforms to a crystalline structure after flame heating. The main hardening mechanism is a result of the precipitation of nanograined diamond membranes, which can be extracted by immersing the flame-hardened Cr–C deposit in an etching solution comprised of 33 vol.% HNO 3 and 67 vol.% HCl.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.