Abstract
Stoichiometric and 2 wt. % excess lead oxide containing lead magnesium niobate (PMN) ceramics have been prepared by partial oxalate route. Dielectric measurements with frequency showed a typical relaxor behavior for stoichiometric PMN, while PMN with excess PbO shows a scatter in the dielectric curves at all temperatures above Tc. Under the same processing conditions, the dielectric constant (Kmax) decreases drastically from 16,300 to 9500 at 1 KHz for PMN without and with excess PbO, respectively. Microstructure studies revealed a second phase (unreacted PbO) segregated in the grain boundaries for excess PbO samples. A careful analysis of the data on dielectric properties and phases present coupled with microstructural detail indicate that the second phase in the grain boundary has a pronounced effect on the dielectric properties and not the pyrochlore phase.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.