Abstract
This paper analyzes the effects of crack tip plastic strains and compressive residual stresses, created by fatigue pre-cracking, on environmentally assisted cracking of pearlitic steel subjected to localized anodic dissolution and hydrogen assisted fracture. In both situations, cyclic crack tip plasticity improves the behaviour of the steel. In the respective cases, the effects are supposed to be due to accelerated local anodic dissolution of the cyclic plastic zone (producing chemical crack blunting) or to the delay of hydrogen entry into the metal caused by residual compressive stresses, thus increasing the fracture load in aggressive environment.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.