Abstract
The present work focuses on the synthesis of inactive mesoporous char using the carbonization method. The experiment was conducted at various conditions using a constant flow of nitrogen gas with variable temperature ramp and carbonization temperature i.e., 5 °C /min to 20 °C /min and 400 °C to 800 °C respectively. The product was identified by calculating its surface area, pore size, micro strain, interplanar spacing, packing density, full-width half maximum, crystallite size, lateral size, no of layers, dislocation density, crystallinity index, and morphological characterization. It was revealed that the best results in terms of surface area, pore size, micropore volume, and burn-off value of the char were observed at a carbonization temperature of 700 °C with a heating rate of 10 °C/min. The calculated values of surface area, pore size, micropore volume, and burn-off were found to be 211.816 m2/g, 2.288 nm, 0.121 cm3/g, and 20.2 % respectively.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.