Abstract
The effect of Ca treatment on hydrogen-induced cracking (HIC) resistance of hot rolled pipeline steel was evaluated. HIC testing was carried out in acidic condition according to NACE standard; results clearly prove that HIC resistance is very sensitive to Ca/S ratio. When Ca/S ratio is below the stoichiometric ratio, HIC occurred at mid-thickness of the steel regardless of the S content. This is closely related to the formation of spherical CaS inclusion with Ca treatment instead of MnS inclusion, which acts on crack initiation sites.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.