Abstract
Groove pressing (GP) has been successfully adopted to achieve fine grain size up to 7μm in AZ31 magnesium alloy with an initial grain size of 55μm. The effect of microstructural evolution and surface features on wettability, corrosion resistance, bioactivity and cell adhesion were investigated with an emphasis to study the influence of deposited phases when the samples were immersed in simulated body fluid (SBF 5×). The role of microstructure was also evaluated without any surface treatments or coatings on the material. GPed samples exhibit improved hydrophilicity compared to the annealed sample. After immersion in SBF, specimens were characterized using scanning electron microscopy (SEM), energy dispersive X-ray (EDAX) analysis and X-ray diffraction (XRD) methods. More amount of white precipitates composed of hydroxyapatite and magnesium phosphate along with magnesium hydroxide was observed on the surfaces of groove pressed specimens as compared to the annealed specimens with an increase in immersion time in SBF. Corrosion behavior of the samples estimated using potentiodynamic polarization curves indicate good corrosion resistance for GPed samples before and after immersion in SBF. The MTT assay using rat skeletal muscle (L6) cells revealed that both the processed and unprocessed samples are nontoxic and cell adhesion was promising for GPed sample.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.