Abstract
The role of bismuth (50 to 9000 ppm) and calcium (50 to 200 ppm) additions on the microstructural characteristics in Sr-modified 319 alloys (with/without 0.4 wt% Mg addition) were investigated using optical and electron microscopy, and image analysis. It was found that the modification effect of Sr continuously diminished with Bi addition up to ~3000 ppm Bi; further Bi addition led to the modification of the Si particles due to the presence of Bi. In the Ca-containing alloys, a coarse eutectic Si structure resulted with Ca additions of 50 ppm, due to the formation of Alx(Ca,Sr)Siy compounds. Increased Ca additions (up to 200 ppm) did not alter the Si particle size. The Alx(Ca,Sr)Siy phase particles appeared in rod-like form in the Sr-modified alloys and in plate-like form in the 319+0.4 wt% Mg alloys. MgO, Al2O3, and AlP particles appear to act as nucleants for the precipitation of the plate-like Alx(Ca,Sr)Siy phase.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.