Abstract
Both hexagonal and cubic calcium aluminate cement (CAC) hydrates react with atmospheric CO 2, bringing about mineralogical changes in concrete, which may, on occasion, lead to loss of mechanical strength. Alkaline hydrolysis or carbonation in the presence of alkalis is a highly destructive process. The purpose of the study was to determine what caused CAC concrete deterioration in a prestressed beam that had suffered intense external damage and showed signs of alkaline hydrolysis or a reaction between the aggregate and the cement. Samples of the internal (sound) and external (damaged) parts of the concrete were studied using XRF, XRD, FTIR, OM, SEM/EDX, and BSE techniques, and mechanical strength was measured on microspecimens extracted from both zones. The conclusion drawn from these analyses was that alkaline hydrolysis took place on or near the surface of the concrete. The white deposits observed around the alkali-containing aggregate were found to consist primarily of bayerite whose very loose consistency undermined the aggregate–matrix bond, greatly weakening the material.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.