Abstract
Abstract In this work, we combined the desirable color characteristics of cationic dyes and the good barrier properties of organoclays by synthesizing hybrid dye-clay nano-pigments (DCNPs) via cationic exchange of two cationic dyes (i.e. basic blue 9 and basic yellow 87) and different commercial organoclays (Cloisite 15A, 20A and 30B). Then, different amounts of synthesized DCNPs were incorporated in an epoxy coating and their corrosion resistance behaviors were investigated by using electrochemical impedance spectroscopy (EIS) and salt spray test. The dry and wet adhesions of samples were measured employing pull-off adhesion test. In addition, the morphology of dispersed DCNPs in epoxy matrix was evaluated by using different techniques including XRD and TEM. Results showed that the extent of intercalation/exfoliation of DCNPs was greater than that of organoclays. Moreover, it was found that DCNPs based on Cloisite 20A had the best dispersion properties among different nanoclays. It was revealed that the corrosion resistance of coatings containing DCNPs (based on Cloisite 20A) was superior in comparison to coatings containing only Cloisite 20A. Finally, results demonstrated the technical feasibility of preparation of colored epoxy coatings with superior corrosion resistance by the incorporation of DCNPs (in the range of 1–5 wt.%) into epoxy matrix.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.