Abstract
The Co1 − (x + y)MgxNiyCr2O4(where, x = y = 0.00, 0.05) nanoparticles were synthesized by the solution combustion technique using a mixture of carbamide and glucose as fuel. The refined XRD study confirmed that samples are single-phased with spinel cubic structure having space group Fd3m. The difference in ionic radius of Co2+ ions and Mg2+, Ni2+ ions resulted in the reduction in lattice parameters. The stretching vibration modes are found at tetrahedral and octahedral site by using FTIR spectra. Force constant value also estimated from FTIR spectra. The magnetic transition was studied by using temperature-dependent magnetization. The magnetic transitions such as ferrimagnetism transition were observed at Curie temperature (TC = 98 K, 91 K for x = y = 0.00, 0.05, respectively), and spiral spin transition was observed at spiral temperature (TS = 26 K, 17 K for x = y = 0.00, 0.05, respectively). Both samples show higher magnetization below spiral transition temperature (TS).
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.