Abstract
Superhydrophobic surfaces have gained sustained attention because of their extensive applications in the fields of self-cleaning, anti-icing, and drag reduction systems. Water droplets must have large apparent contact angle (CA) (>150°) and small CA hysteresis (<10°) on these surfaces. However, previous research usually involves complex fabrication strategies to modify the surface wettability. It is also challenging to maintain the temporal and mechanical stability of the delicate surface textures. Here, we develop a one-step solvent-free sand-in method to fabricate robust superhydrophobic surfaces directly atop various substrates with an apparent CA up to ∼163.8° and hysteresis less than 5°. The water repellency can withstand 100 Scotch tape peeling tests and remain stable after being stored under ambient humid conditions in Houston, Texas, for 18 months or being heated at 130 °C in air for 24 h. The superhydrophobic surfaces have excellent anti-icing ability, including a ∼2.6× longer water freezing time and ∼40% smaller ice adhesion strength with the temperature as low as -35 °C. Since the surface layers are fabricated by sanding the substrates with the powder additives, the surface damage can be repaired by a direct re-sanding treatment with the same powder additives. Further sand-in condition screenings broaden surface wettability from hydrophilic to superhydrophobic. The sand-in method induces the surface modification and the formation of the tribofilm. Surface and materials characterizations reveal that both microstructures and nanoscale asperities of the tribofilms contribute to the robust superhydrophobic features of sanded surfaces.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.