Abstract
The thermodynamic stability of the premartensite (PM) phase has been a topic of extensive investigation in shape memory alloys as it affects the main martensite phase transition and the related physical properties. In general, the PM phase is stable over a rather narrow temperature-composition range. We present here evidence for chemical pressure induced suppression of the main martensite transition and stabilization of the PM phase over a very wide temperature range from 300 K to around 5 K in a magnetic shape memory alloy (MSMA) Ni50Mn34In16 using magnetic susceptibility, synchrotron X-ray powder diffraction (SXRPD) studies and first-principles calculations. The ac-susceptibility studies show a highly skewed and smeared peak around 300 K without any further transition up to the lowest temperature of our measurement (5 K) for around 5% Al substitution. The temperature evolution of the SXRPD patterns confirms the appearance of the PM phase related satellite peaks at and below 300 K without any splitting of the main austenite (220) peak showing preserved cubic symmetry. This is in marked contrast to the temperature evolution of the SXRPD patterns of the martensite phase of the Al free as well as around 3% Al substituted compositions where the austenite (220) peak shows a clear splitting due to Bain distortion/symmetry breaking transition. Our theoretical calculations support the experimental findings and reveal that the substitution at the In site by a smaller size atom, like Al, can stabilize the PM phase with preserved cubic symmetry. Our results demonstrate that Al-substituted Ni-Mn-In MSMAs provide an ideal platform for investigating the physics of various phenomena related to the PM state.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.