Abstract
The present study focuses on developing lightweight assembly of two different aluminium alloys extruded and high pressure die cast (HPDC) for battery frame assembly in BEV. The goal is to produce defect-free welds in lap configuration with smooth surface finish. Stationary shoulder friction stir welding (SSFSW) was employed with welding speeds of 3–15 mm/s. EBSD analysis revealed two groups of grains in the stir zone (SZ) due to dynamic recrystallization. Moreover, the grain size of the SZ significantly decreased compared to both alloys. The cast alloy contains large iron particles, and that were broken by the rotating probe, and the stirred material consisted of fine dispersed precipitates. Tensile-shear test found the fracture location at the hook area near to cast, and a model representing fracture behavior is also discussed. With increasing welding speed from 3 to 5 mm/s, the tensile strength found ∼95 and ∼100 MPa, respectively without any significance difference in the fracture behavior and location. Overall, this study provides valuable insights such as materials mixing, grain refinement, and joint strength in dissimilar joining using SSFSW. The findings could be useful in developing optimized welding parameters and improving the overall quality and productivity of the SSFSW process for battery pack assembly in BEV.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.