Abstract
Polycrystalline Bi0.8Sr0.2Fe1 − xTixO3 (x = 0.0, 0.1, 0.2) multiferroics were synthesized via the conventional solid state reaction method. The structure, dielectric relaxation, and magnetic properties of as prepared samples were investigated. The crystal structure examined via XRD and Rietveld analysis confirmed a single phase rhombohedral (space group R3c no. 161) structure. In the Rietveld refinement, good agreement between the observed and calculated pattern was observed. The dielectric response of these multiferroics was analyzed in the frequency range of 10 Hz to 5 MHz at different temperatures. All the samples showed dispersion in dielectric constant (έ) and dielectric loss factor (tan δ) values. The temperature dependence of έ and tan δ showed broad peaks. A reduction in the values of έ and tan δ was observed upon the incorporation of Ti. Magnetic measurements were carried out at room temperature up to a field of 20 kOe. Magnetic hysteresis loops revealed a significant increase in magnetization with Ti substitution. A remnant magnetization (Mr) of 33.428 memu/g and a coercive field (Hc) of 1.724 kOe were observed in the sample with x = 0.2.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.