Abstract
Rice straw cellulose microfiber (CMF) was obtained through the gentle low-temperature phase transition method. Then, NaIO4 was utilized to modify CMF by selective oxidation to prepare aldehyde CMF (a-CMF) to improve the reactivity of the CMF. Finally, the a-CMF reinforced polyvinyl alcohol (PVA) composite films were prepared through a pre-cross-linking and solvent casting approach. The cross-linking network formed by a-CMF and PVA through the aldolization reaction significantly improved the mechanical properties of the a-CMF/PVA composite film. The tensile strength of a-CMF-2/PVA was 37.54 ± 0.77 MPa, which was higher than 25.88 ± 2.97 MPa of the pure PVA. SEM results showed that the fracture surface of the a-CMF/PVA composite film with the cross-linking network was smooth. In addition, prepared a-CMF-2/PVA composite films had a transmittance of over 80 % in the visible light range, and also possessed excellent UV blocking property.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.