Abstract
In this study the effect of nano sized silica particles (nano-SiO2) on the physical and mechanical properties of rice husk and Old Corrugated Container (OCC)-cement boards was investigated. Modulus Of Rupture (MOR), Modulus Of Elasticity (MOE), Internal Bonding Strength (IB), density, water absorption and thickness swelling after 24 hours immersion in water and hardness were measured. Results showed that rice husk-cement boards with 2% nano-SiO2 demonstrated the best physical and mechanical properties. It is related to better distribution and compaction of particles during compression without particles agglomerating. A higher property of 2%-nano-SiO2 content rice-husk-cement boards was confirmed by their higher hydration temperature. Addition of 3% nano-SiO2 to the mixture reduced the density because of both the substitution of denser cement particles by lighter nano-SiO2 particles and air-entrapment in the boards. Furthermore, Scanning Electron Microscopy (SEM) analyses showed that the optimum amount of nano-SiO2 (2%) can fill micro pores and make a uniform structure with a rough surface which improves properties of composite boards.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callMore From: Iranian Journal of Chemistry & Chemical Engineering-international English Edition
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.