Abstract

Thermoplastic starch was blended with commercially available biodegradable polyesters of poly(butylene adipate-co-terephthalate) (PBAT) and poly(lactic acid) (PLA) for its improved performance and processability. The morphology and elemental composition of these biodegradable polymer blends were observed by scanning electron microscopy and energy dispersive X-ray spectroscopy, respectively, while their thermal properties were analyzed using thermogravimetric analysis and differential thermal calorimetry. For rheological analysis, the steady shear and dynamic oscillation tests of three samples at various temperatures were investigated using a rotational rheometer. All three samples exhibited significant shear thinning at all measured temperatures, and their shear viscosity behavior was plotted using the Carreau model. The frequency sweep tests showed that the thermoplastic starch sample exhibited a solid state at all temperatures tested, whereas both starch/PBAT and starch/PBAT/PLA blend samples exhibited viscoelastic liquid behavior after the melting temperature such that their loss modulus at low frequencies was greater than the storage modulus, and inversion occurred at high frequencies (storage modulus > loss modulus).

Talk to us

Join us for a 30 min session where you can share your feedback and ask us any queries you have

Schedule a call

Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.