Rheological Behavior of a Novel Organic-Inorganic Hybrid: Micro/Nano-Tin Fluorophosphate Glass-Polycarbonate.

Abstract

The rheological behavior of a novel, binary organic-inorganic hybrid consisting of an ultra-low Tg tin fluorophosphate glass (Pglass) and polycarbonate (PC) was investigated using oscillatory rheometry. It was found that the complex viscosity of the hybrid showed Pglass content dependence. Under low Pglass content (10-30%), the complex viscosity of the hybrid was lower than that of pure PC. While the complex viscosity was dramatically increased and higher than that of pure PC with the content of Pglass above 30%. This phenomenon was particularly remarkable at low frequencies. Besides, with the addition of Pglass the hybrid material exhibited shear-thinning behavior and the shear-thinning characteristics became more obvious with the enhancement of the Pglass content, indicating the presence of nonlinear chemical and physical interactions between the hybrid components. Differential scanning calorimetry (DSC) measurements revealed that increasing the content of Pglass caused a decrease of the glass transition temperature (Tg) of the hybrids, suggesting that Pglass was acting as a macromolecular plasticizer for the PC. The microstructure of the Pglass in the hybrid material was characterized by scanning electron microscopy (SEM). The results showed that the Pglass were dispersed as micro- and nano-bead in the continuous phase of PC and the Pglass appeared aggregation partly with the increase of the Pglass content. This contribution was anticipated to be a guideline for the processing of this promising new class of hybrid materials.