Abstract
It is still an open debate whether the 1:5H cell boundaries (CBs) or the intersections of 1:3R platelets and 1:5H CBs are the strong pining sites for the cellular nanostructured 2:17-type Sm-Co-Fe-Cu-Zr high temperature permanent magnets despite that they have been widely applied in advanced industries since 1970s. Herein, through tuning the volume fraction of Zr-enriched 1:3R platelets by varying the second-step aging time, the pinning behavior in a model magnet Sm25Co44.9Fe21.5Cu5.6Zr3.0 (wt%) was investigated. The results show that the volume fraction of 1:3R platelets can be effectively enlarged without changing the cell size (i.e. the volume fraction of CBs) by extending the aging time at 400 °C. Microscopic TEM characterizations combined with macroscopic magnetic measurements reveals that the locally thickened 1:3R platelets after long-term second-step aging reduce the effective pinning area by interrupting the magnetic domain walls at CBs, weakening the average pinning strength and the coercivity of the magnet. Consequently, our work supports that the 1:5H CBs act as the dominating pinning sites instead of the intersections of 1:3R platelets and 1:5H CBs, which may provide an important insight towards understanding the hard magnetism of pinning-controlled permanent magnets.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.