In this present study, TiO2 nanofilms were deposited at 773 K by using titanium tetra isopropoxide as precursor and ethanol as solvent with the variation of pH for x = 2.50, 6.50, and 10.50 through automated nebulizer spray pyrolysis (ANSP) technique. The properties of Structural (XRD), Topography (AFM) and surface morphology (FESEM) of the film shows the average particle size, average roughness and particle shape were drastically changed with respect to electrolyte pH parameter. Anatase phase of polycrystalline tetragonal structure was revealed by structural (XRD) and X-ray photoelectron study (XPS). The XPS study confirms the films that not detected with the other trace of impurity except carbon. The optical transmittance decreased at higher pH and their band gap energy in the range of 3.29–3.43 eV was obtained with the change in electrolyte pH parameter for all the TiO2 film. The electrical study of dielectric constant, tan δ is continue to decrease with increase the frequency and the maximum dielectric constant and tan δ value observed as ∼41.73 and ∼03.62 for pH = 6.50. The adsorption and desorption of various gas sensing performance of TiO2 film were analysed with the function of temperature and the high sensing response of NH3 where noted.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.