Abstract
Reversible topotactic transitions between oxygen-vacancy-ordered structures in transition metal oxides provide a promising strategy for active manipulation of material properties. While transformations between various oxygen-deficient phases have been attained in bulk ABO$_{3-\delta}$ perovskites, substrate clamping restricts the formation of distinct ordering patterns in epitaxial films. Using in-situ scanning transmission electron microscopy (STEM), we image a thermally driven reversible transition in La$_{0.5}$Sr$_{0.5}$CoO$_{3-\delta}$ films on SrTiO$_3$ from a multidomain brownmillerite (BM) structure to a uniform phase wherein oxygen vacancies order in every third CoO$_x$ plane. Because temperature cycling is performed over a limited temperature range (25 {\deg}C - 385 {\deg}C), the oxygen deficiency parameter $\delta$ does not vary measurably. Under constant $\delta$, the topotactic transition proceeds via local reordering of oxygen vacancies driven by thermal strain. Atomic-resolution imaging reveals a two-step process whereby alternating vertically and horizontally oriented BM domains first scale in size to accommodate the strain induced by different thermal expansions of La$_{0.5}$Sr$_{0.5}$CoO$_{3-\delta}$ and SrTiO$_3$, before the new phase nucleates and quickly grows above 360 {\deg}C. Upon cooling, the film transform back to the mixed BM phase. As the structural transition is fully reversible and $\delta$ does not change upon temperature cycling, we rule out electron-beam irradiation during STEM as the driving mechanism. Instead, our findings demonstrate that thermal strain can solely drive topotactic phase transitions in perovskite oxide films, presenting opportunities for switchable ionic devices.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.