Abstract
The fabrication and processing of an actuator with a TiNi Shape Memory Alloy (SMA) film are discussed and demonstrated. TiNi SMA films were deposited by using sputter deposition techniques, patterned and etched. These films were solution-treated and aging-treated, and then an inverse force layer of chromium was deposited on a SMA film. The frequency response of the beam type actuator was measured by resistance heating. The maximum amplitude was in proportion to the inverse force, and was therefore controlled by chromium thickness. The maximum displacement slightly decreased with an increase of frequency. The minimum displacement suddenly increased at more than 0.1 Hz, then showed a stability over 5 Hz. The maximum displacement was not decided by chromium thickness but TiNi thickness, because thickness of the latter was fifteen to forty times larger than that of the former. Because the frequency response depended on the heat radiation of an actuator, TiNi thickness was the most important factor to the actuation.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.