Reversible multielectron redox in NASICON cathode with high energy density for low-temperature sodium-ion batteries

Abstract

The NASICON-type Na3V2(PO4)3 cathode based on vanadium multiple redox is particularly attractive for large-scale sodium-ion battery application. In this work, it was found that the reversible redox of V4+/V5+ can be activated by replacing a part of V3+ with Al3+, obtaining Na3V1.5Al0.5(PO4)3 with typical NASICON phase structure and offering a reversible specific capacity of 163 mAh g−1 through a three-electron redox reaction with a small volume change (2.62%). The most surprising thing is that in addition to favorable room temperature electrochemical performance, Na3V1.5Al0.5(PO4)3 also exhibits a superior low temperature (-20 °C) cycling stability with a capacity retention of 98.9% after 1000 cycles at 5 C. Thin and conformal CEI film as well as stable phase structure across a broad temperature range are responsible for this superior electrochemical property. A Na+ storage mechanism consisting of two-phase and solid-solution electrochemical reactions for Na3V1.5Al0.5(PO4)3 cathode is elucidated via ex-situ XRD structural analysis. DFT calculations indicate that Al3+ substitution could manipulate the localized electronic state and strengthen the oxygen ligand skeleton in the NASICON matrix. Hence, the Na3V1.5Al0.5(PO4)3 cathode renders a slight lattice variation upon the repeated desodiation and sodiation and enhanced Na+ diffusion rate along with low charge transfer resistance.