Reversible Modification of CdSe–CdS/ZnS Quantum Dot Fluorescence by Surrounding Ca2+ Ions

Abstract

It has been known for a long time that the fluorescence intensity of colloidal quantum dots (QDs) becomes modified when free ions are added to the QD solution. The consequences of removing free ions from the QD solution, however, have not been closely investigated. In this work we studied fluorescence from 3-mercaptopropionic acid (3-MPA) coated CdSe–CdS/ZnS core–multishell QDs when free Ca2+ ions were added to and subsequently removed from the QD solution. It was found that QD fluorescence intensity was reduced when Ca2+ ions were added to the QD solution, while the wavelength of the QD fluorescence peak remained unchanged. QD fluorescence recovered when the concentration of free Ca2+ ions in the QD solution was reduced by adding Ca2+ chelator (ethylene glycol tetraacetic acid, EGTA). It was further observed that the time of single QD fluorescence at on-state and QD fluorescence lifetimes were also reduced after adding Ca2+ and then recovered when EGTA was added. Theoretical study shows that a free Ca2+ ...