Revealing the dimensional stability mechanisms of SiC/Al composite under long-term thermal cycling

Abstract

Long-term thermal cycling causes irreversible dimensional changes of the material, which in turn affects the reliability of precision instruments. In this paper, dimensional stability mechanisms of SiC/Al composites during thermal cycling were revealed using high-precision thermal dilatometer, XRD and spherical aberration correction transmission electron microscope (Cs-TEM). First, how the factors including dislocations, internal stress and precipitates affect the dimensional change of SiC/Al composites were separately introduced. Then, the integrated effect of these factors affecting the dimensional stability of SiC/Al composites was further discussed. Among them, the integrated effect of dislocation-internal stress in SiC/pure Al composites leads to an increase in dislocation density and average lattice constant, which leads to an increase in dimensional change. The integrated effect of dislocation-internal stress-precipitates in SiC/2024Al composites leads to a decrease in the average lattice constant and some changes in the precipitation behavior (including the type, density and lattice constant of the precipitates), which ultimately leads to a decrease in dimensional change. The dimensional change of the two types of composites was semi-quantitatively estimated. Finally, the reasons for the significantly higher dimensional stability of the SiC/2024Al composites were given.