Abstract
Metals containing abundant coherent twin boundaries (TBs) are able to sustain substantial plastic deformation without fracture due to shear-induced TB migration and sliding. Retaining ductility in these metals, however, has proven difficult because detwinning rapidly exhausts TB migration mechanisms at large deformation, whereas TB sliding was only evidenced for loading on very specific crystallographic orientations. Here, we reveal the intrinsic shear deformability of twins in nanocrystals using in situ nanomechanical testing and multiscale simulations and report extreme shear deformability through TB sliding up to 364%. Sliding-induced plasticity is manifested for orientations that are generally predicted to favor detwinning and shown to depend critically on geometric inhomogeneities. Normal and shear coupling are further examined to delineate a TB orientation-dependent transition from TB sliding to TB cracking. These dynamic observations reveal unprecedented mechanical properties in nanocrystals, which hold implications for improving metal processing by severe plastic deformation.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.