Abstract
The effect of prior single tensile overloading on the stress corrosion cracking behavior of cold rolled 316L in a simulated PWR water environment at 310 °C was investigated. SCC growth retardation by overloading was observed in cold rolled 316L specimens in both the T-L and L-T orientations. The stretch zone observed on the fracture surfaces of the overloaded specimens affected SCC propagation. The compressive residual stress induced by overloading process reduced the effective driving force of SCC propagation. The negative dK/da effect ahead of the crack tip likely contributes to the retardation of SCC growth. The duration of overloading is dependent on water chemistry and the local stress conditions.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.