Abstract
AbstractUsing very-high-frequency (VHF) plasma decomposition of SiH4 and pulsed gas technique, we have successfully prepared nanocrystalline silicon (nc-Si) quantum dots having average diameter of 8 nm and dispersion of 1 nm. The role of natural oxide is very important. It controls the size of nc-Si dots. Of particular interest is that the oxidation of these dots can be self limited, due to the stress induced near Si/oxide interface, which would allow further reduction of size and improvement in dispersion. This paper deals with the systematic study of oxidation process of nc-Si dots. Nc-Si dots formed in an Ar plasma with SiH4 gas pulses are deposited onto a Pt mesh The dots are then oxidized at 750, 800 and 850°C from 20 minutes to 15 hours. The dimensions of the residual nc-Si and the grown oxide are measured directly from the TEM micrographs and analyzed. For comparison, field oxide is investigated using ellipsometry. Retardation in the oxidation rate of nc-Si is observed. The mechanism of the reduction of oxidation rate in nc-Si is discussed taking into account the effect of stress.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.