Abstract
Silicon nitride ceramics were prepared by means of a hot-press sintering method. The ablation behavior was studied by plasma wind tunnel tests. The data suggested that, under low heat flux and stagnation pressure conditions, the ablation process was controlled by the atomic oxidation of Si3N4, leading to the elimination of Si3N4. By contrast, the erosion was mainly produced by the decomposition of Si3N4 under high heat flux and stagnation pressure conditions. Under these conditions, a fraction of Si phase, formed upon decomposition of Si3N4, was volatilized. The remained Si had melted due to high temperatures and scoured away from stagnation point area, generating mushroom-shaped samples.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callMore From: Journal of Wuhan University of Technology-Mater. Sci. Ed.
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.