Abstract
The present investigation deals with performance of coir fibre reinforced cement boards subjected to matrix modification by silane-based water repellent chemical additive and microwave accelerated curing (MC). The fibre-cement boards were tested for water absorption, modulus of rupture (MOR) and modulus of elasticity (MOE). Scanning electron microscopy (SEM) and Fourier-transform infrared spectroscopy (FTIR) were used to characterize the composite samples. 84% reduction in water penetration was achieved through the use of the water repellent additive while MC samples had higher MOR and MOE values than the water cured samples. SEM characterization showed that MC provided good interfacial adhesion between the matrix and the reinforcement while the chemical additive reduced the occurrence of voids and pores on the surface. FTIR indicated prominent bands at 3423, 1425.44 and 875.41 cm−1 which are indicative of O–H stretching of the portlandite, C-H denoting the lignin deformation with aromatic ring stretching and C-O representing bend of carbonates. Therefore, MC and use of water repellent additive are recommended to improve the performance of cellulose fibre cement based applications.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.