Abstract
In this study, YBa2Cu3O7―x/Nb:SrTiO3 (YBCO/Nb:STO) planar heterostructure was prepared on Nb:SrTiO3 (Nb:STO) substrate by sol-gel method. The I–V curves revealed that the structure exhibited excellent resistive switching (RS) effect. Current transmission characteristics of the heterostructure prepared using different electrodes and Nb:STO were analyzed. Results indicated that the RS effect was caused by the capture and escape of the electrons from the charge trap at the interface between electrode and Nb:STO. Schottky barrier was a prerequisite for the RS effect. Further investigation of the current transport properties of the YBCO/Nb:STO heterostructure at low temperature revealed that the current transport was affected by its own carriers and charge traps when the heterostructure was under low-resistance state, and the current decreased with decreasing temperature. Owing to the decrease in barrier height, the current increased with decreasing temperature under high-resistance state, with current transport properties exhibiting Schottky emission characteristics.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.