Abstract
In this study blended cements containing corncob ash (CA) and ground granulated blast furnace slag (GGBFS) were investigated. The blended cements were prepared using a clinker, 5% gypsum by weight CA and GGBFS. Different amounts of additives (20 and 40%) were incorporated into these blends in equal amounts. Control cement, that is, plain Portland cement, without any additions, was also prepared and studied in order to establish the effects of additives to cement. Clinkers from Adana, Cimsa and Mardin were used. CA was obtained by burning corncob waste and had a 500 m²/kg Blaine value, and GGBFS was ground to give a Blaine value of 300 m²/kg for all cements. The compressive strengths were measured for 3, 7, 28, 90, and 180 days in tap water. Their sulfate resistance was determined by compressive strengths after 24 months under sulfate conditions. CA and GGBFS gave an activity index grades of 80 and 71%, respectively. The microstructures and morphology of plain and blended cements were studied by scanning electron microscopy. The micrographs showed that these additives provide more condense structures of cement hydration and excellent sulfate resistance. Thus, CA and GGBFS additives in cement production can contribute to the cement durability. Key words: Blended cements, corncob ash, ground granulated blast furnace slag, sulfate.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.