Resistance of glaze application on indirect restorative CAD/CAM materials against abrasive toothbrushing wear.

Abstract

The aim of this study was to evaluate the effect of toothbrushing on the surface roughness (Sa), roughness profile (Rv), gloss units (GU) and surface morphology of three glazed ceramics. Specimens (n=7) from different CAD/CAM materials 1- Lithium disilicate-based glass ceramic (IPS e.max CAD); 2- Zirconia-reinforced lithium silicate glass ceramic (Celtra Duo) and 3- 6 mol% yttria partially-stabilized zirconia (InCoris) were evaluated. IPS e.max CAD and InCoris specimens were sintered and all the groups were pre-polished and glazed according to the manufacturer's recommendations: IPS Ivocolor Glaze Paste (Ivoclar Vivadent) or Universal Overglaze High Flu (Dentsply/Sirona). Sa, Rv, GU and morphology were analyzed before and after brushing at 30.000, 120.000 and 180.000 cycles. The data of Sa and GU were analyzed by ANOVA two-way and post-hoc Tukey's test (α=0.05). Rv was analyzed by Kruskal-Wallis and Student-Newman-Keuls. The surface morphology was analyzed qualitatively. The Sa decreased significantly after 180.000 toothbrushing cycles for all materials tested. CE showed higher Rv than EM and IN, and IN showed the highest GU after 180.000 toothbrushing cycles, which promoted a polishing effect for all materials. Long-term toothbrushing was not able to jeopardize the glazed-surface of all tested materials compared to unbrushed.