Abstract
The aim of this work is to evaluate the welding residual stress profile in ASTM A106 Gr. B steel pipes with 4 diameter and to correlate this profile with the microstructure and hardness of the joint. The results showed that the residual stresses are more uniform for a lower welding heat input. Higher welding heat input causes not only a non-uniformity of the stress profile but also promotes the maximum stress as high as the yield strength. The microstructure was composed of ferrite, perlite and possibly bainite; the presence of martensite was not verified. The hardness results indicated that none of the welding parameters used produced levels of hardness greater than 249 HV. Such a result is of fundamental importance because it suggests that low hardness does not necessarily mean low residual stress levels.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.