Abstract
A NiCoCrAlY bond coating was low-pressure plasma sprayed on a stainless steel sub- strate. Zirconia with 8 wt% yttria was deposited on the bond coating using an electron beam-physical vapor deposition (EB-PVD) method. The top coating had the preferred orientation with the h111i axis direction perpendicular to the coating plane. The distribution of the in-plane residual stress in the top coating was measured using laboratory Cr-K X-rays with a progressive layer removal method. The value of the in-plane stresses was determined by the sin2 method after the separation of the 133 and 331 peaks. The distribution of the out-of-plane strain in the top coating was measured using the strain scanning method with hard synchrotron X-rays. The out-of-plane strain was obtained from the 333 peak which had strong intensity due to the preferred orientation. The measured value of the in-plane stress in the top coating was a large compression, and showed a steep decrease near the in- terface between the top and the bond coatings. The distribution of the out-of-plane stress showed a compression, and its magnitude was smaller than that of the in-plane stress.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.